Mark arc welding metal surface arc welder can cause a rough surface defects. Protective film damage, leaving a potential source of corrosion. Arc welder should have been welded in the weld bead or weld joints in the side. And then melt into the weld arc traces. Spatter Spatter have a great relationship with the welding process. For example: GTAM (Gas Tungsten Arc Welding) or TIG (tungsten inert gas welding) does not spatter. However, when using GMAW (gas metal arc welding) and FCAW (flux cored arc welding with the) two welding process of welding parameters if used improperly can cause a lot of splatter. When this occurs, you must adjust the parameters. If you want to solve the problem of weld spatter, before welding the joint should be painted on each side of the splash agent, thus eliminating the adhesion of spatter. After welding can easily various agents such splash spatter clean out, do not damage the surface or bring minor injuries. Pitting, crevice corrosion and stress corrosion under certain conditions performance. The biggest factor of between austenitic stainless steel to intergranular corrosion susceptibility effect is carbon content, stainless steel car axis design, other elements intergranular corrosion effects depending on the primary influence on the behavior of dissolution and precipitation of carbides may be, in austenitic stainless steel, stainless steel car axis price, chromium can increase the solubility of carbon and reduce the degree of chromium depleted, thus improving resistance to intergranular corrosion is useful chromium content of austenitic stainless steel, stainless steel car axis, chromium is very effective austenitic stainless steel to improve resistance to pitting and crevice corrosion, when the steel while molybdenum or molybdenum and nitrogen exists, this strengthening of the effectiveness of large chrome, stainless steel car axis classification, although according to the pitting corrosion Molybdenum and crevice corrosion is about three times as chromium, chromium nitrogen 30 times, but a lot of research, austenitic stainless steel is low if there is no chrome or chromium content of molybdenum and resistance to pitting corrosion and crevice corrosion nitrogen action will loss or significant enough. Stainless steel car axis _ _ Shengyuan precision stainless steel car axis provided by the Dongguan City Shengyuan Stainless. Stainless steel car axis _ _ Shengyuan precision stainless steel car axis Dongguan City Shengyuan Stainless (dg-shengyuan.cn) this year introduced a new upgrade, the above picture is for reference only, please call the contact picture on this page or telephone obtain the latest information, contact: Liang Ye.